Micrometer-size crystalline monolayer MoS2 domains obtained by sulfurization of molybdenum oxide ultrathin films

  • Autori: Panasci S.E.; Schiliro E.; Koos A.; Nemeth M.; Cannas M.; Agnello S.; Roccaforte F.; Pecz B.; Giannazzo F.
  • Anno di pubblicazione: 2023
  • Tipologia: Articolo in rivista
  • OA Link: http://hdl.handle.net/10447/589292

Abstract

In this work, the formation of micrometer-size crystalline monolayer (1L) MoS2 flakes with triangular shape and a central multilayer core is obtained by the sulfurization at 800 °C of pre-deposited ultrathin MoOx films (1.2–1.8 nm) on c-sapphire substrates. The thickness uniformity, crystalline quality, doping and strain distribution in the MoS2 flakes as a function of the initial MoOx thickness was evaluated by micro-Raman (μR) mapping. The excellent crystalline quality of the triangular 1L-MoS2 flakes was confirmed by micro-photoluminescence (μPL) maps, showing a very intense peak at ∼1.85 eV, that decreases in the central part, as expected for multilayers MoS2. A biaxial strain of ∼0.38–0.4% was deduced from the μPL data, in perfect agreement with μR results. Our results show how the sulfurization of pre-deposited MoOx films on c-sapphire allows, under proper conditions, to obtain 1L-MoS2 flakes with quality comparable to the one typically reported by the conventional chemical vapour deposition, with important implications for device applications.